 another welding question, how bad is it... stainless to steel |
|
|
|
Porsche, and the Porsche crest are registered trademarks of Dr. Ing. h.c. F. Porsche AG.
This site is not affiliated with Porsche in any way. Its only purpose is to provide an online forum for car enthusiasts. All other trademarks are property of their respective owners. |
|
|
| brant |
 Apr 25 2005, 03:47 PM
Post
#1
|
|
914 Wizard  Group: Members Posts: 11,771 Joined: 30-December 02 From: Colorado Member No.: 47 Region Association: Rocky Mountains 
 |
Ok...
how bad did I screw up the metals? what is the correct way (type of wire, type of shielding gas) to weld Stainless steel and regular steel? to top it off this was a piece of galvanized pipe no less: Attached thumbnail(s) 
|
   |
 
|
  |
Replies(1 - 6)
| TimT |
Apr 25 2005, 04:01 PM
Post
#2
|
|
retired Group: Members Posts: 4,033 Joined: 18-February 03 From: Wantagh, NY Member No.: 313 |
I wouldnt worry about it... it might not be the prettiest weld, but Im sure it will serve its function
|
|
|
|
| lapuwali |
Apr 25 2005, 04:50 PM
Post
#3
|
|
Not another one! Group: Benefactors Posts: 4,526 Joined: 1-March 04 From: San Mateo, CA Member No.: 1,743  |
That looks like an exhaust fitting, and if so, I'd agree with Tim. You mostly have to worry about stainless welding in structural applications. Any cracks that develop in an exhaust are usually just annoying, not life-threatening.
|
|
|
|
| scotty b |
Apr 25 2005, 05:44 PM
Post
#4
|
|
rust free you say ? Group: Members Posts: 16,375 Joined: 7-January 05 From: richmond, Va. Member No.: 3,419 Region Association: None |
It will werk just fine but for future reference CLEAN the galvanizing off first that stuff is VERY toxic. Second use stainless wire (mig) or filler rod Tig or gas) and when using filler rod get the closest to the same stainless alloy you are using.If'n you don't know the alloy go with 304 it is more or less universal.
|
|
|
|
| John Kelly |
Apr 26 2005, 06:56 AM
Post
#5
|
|
Senior Member Group: Members Posts: 692 Joined: 1-May 03 From: Moclips WA. Member No.: 640 |
That weld turned out nice (could have been a wee bit hotter) especially considering the galvanized...hate that stuff.
John www.ghiaspecialties.com |
|
|
|
| brant |
Apr 26 2005, 10:08 AM
Post
#6
|
|
914 Wizard Group: Members Posts: 11,771 Joined: 30-December 02 From: Colorado Member No.: 47 Region Association: Rocky Mountains
|
Thanks guys..
I knew it wasn't going to be the best.... but it is an exhaust and I figured at worst it might crack or something... (it was on a sunday and I didn't have any correct wire, helium, or ability to go buy any.... ) thanks for the tips too. I love this place. I learn a ton from you guys. brant |
|
|
|
| Brett W |
Apr 26 2005, 10:41 AM
Post
#7
|
|
Advanced Member Group: Members Posts: 2,858 Joined: 17-September 03 From: huntsville, al Member No.: 1,169 Region Association: None
|
When welding stainless you need to run a purge gas through the backside of the weld. This will keep the "sugar" from forming on the backside and creating a weak spot. But in your application I wouldn't worry about it.
Brant and others when welding anything galvanized you must clean it well. The fumes created from welding a galvanized piece can cause cancer and other bad problems. I don't know if this works on all galvanizing but it will work on CAD plated parts. Fill a small container with Sno-Bowl toilet cleaner. Set this container outside as very hazardous fumes willbe given off, and then dip your parts in it and let them sit there. A violent chemical reaction will take place and completely remove the CAD plating. |
|
|
|
|